DM-OC-6031S is a screen printed high transparency overcoat ink (>99%) that offers exceptional levels of durability. The ink is typically used in conjunction with our transparent conductive ink, DM-SNW-8012S for applications such as display, PV, capacitive switch, sensors, lighting and transparent heaters.

£95.10£198.90

p

Sample pricing available for on-line purchasing only, please contact us directly for competitive bulk pricing

New
Availability: usually ships within 5 days

Product Description

DM-OC-6031S is a transparent, screen printable paste for use with Dycotec’s range of conductive transparent ink systems providing high levels of durability. It is screen printable and thermally cured.

Product Benefits

• Formulated for screen printing
• Excellent transparency
• Protective overcoat for Dycotec’s range of transparent conductive pastes
• Excellent printability
• Low temperature cure

Paste Preparation

DM-OC-6031S is a single part paste system. Once the paste has been removed from the container for printing, this may introduce contamination. Please do not replace the paste in the container. The paste should be gently stirred before use
avoiding incorporation of air bubbles. Avoid paste drying on screen, use flood-print-flood process to avoid drying.

 

Additional information

More
Size (g)

100g, 250g, 1Kg

Viscosity after mixing (Pa.s)

0.3 – 0.8

Substrate

PET

Screen

325 SS, 23 µm EOM or P120/31 polyester, 21 µm EOM, 13 μm emulsion, 325 DPI

Flood Speed

70 mm/s

Print Speed

70 mm/s

Squeegee Hardness

80A Durometer Shore

Cure Process

Convection oven or IR heating

Cure Temperature (oC)

80-100˚C

Cure Time (mins)

10-20 mins

Adhesion

5B

Transparency

>99%

WeightN/A

Still Unsure?

Development

We offer a tailored formulation development service to meet specific customer overcoat requirements.  We have experience of developing systems for specific customer applications, with different properties including:
  • Barrier Layer
  • Chemical resistance
  • High temperature resistance
  • Rheology changes to enable use of different deposition techniques
  • Hydrophobic surfaces
  • Flexibility
  • Polyurethane, silicone and epoxy systems
  • Optical characteristics including additional of phosphorescent/fluorescent additives

Applications

  • Sensors
  • Lighting
  • Display
  • Solar Cell
  • Transparent Heaters
  • Capacitive Switching